Laurel Low cement castable is based on low calcium aluminate cement content, and they are used in many applications that require high refractoriness, corrosion resistance and abrasion resistance. They possess a uniform structure with low porosity; have high-temperature strength throughout the low and intermediate temperature ranges.The content of CaO of low cement castable is usually less than 3%,so it ensures the castable has a good strength in mid-temperature.
Item | LALC75 | LALC80 | LALC85 | LALC95 |
Service Temp ºC | 1650 | 1700 | 1750 | 1780 |
Bulk Density (g/cm3) (Dried at 110ºC) |
2.55 | 2.6 | 2.7 | 3.0 |
CCS 110ºC (Mpa) 1100ºC 1500 ºC |
65 75 80 |
70 80 85 |
80 90 100 |
90 95 110 |
MOR 110ºC (Mpa) 1100ºC 1500ºC |
9 10 11 |
10 11 12 |
11 12 13 |
13 14 15 |
Max Grain Size (mm) | 6 | 6 | 6 | 6 |
Chemical Analysis(%) Al2O3 CaO Fe2O3 |
75 2-3 2.4 |
80 2-3 2.0 |
85 2-3 1.8 |
95 2-3 1.5 |
Application Guidelines Mixer Placement Water/Mixer TempºC Mixing Time(Min):Dry/Wet |
P V/T 20±5 2/5 |
P V/T 20±5 2/5 |
P V/T 20±5 2/5 |
P V/T 20±5 2/5 |
Water % (Typical) | 7-9 | 7-9 | 6-8 | 6-7 |